| Melt flow rate at 230 °C/3.8 Kg | 2 | g/10min | ISO 1133 | -- |
| Shrinkage | 0.2 - 0.6 | % | ISO 294 | -- |
| Water absorption at 24hr | 0.3 | % | ISO 62 | -- |
| Density | 1.19 | g/cm3 | ISO 1183 | -- |
| Tensile strength at 5 mm/min | 77 | mPa | ISO 527 | -- |
| Tensile Modulus at 1 mm/min | 3300 | mPa | -- | -- |
| Elongation at 5 mm/min | 6 | % | -- | -- |
| Flexural Strength at 2 mm/min | 135 | mPa | ISO 178 | -- |
| Flexural Modulus at 2 mm/min | -- | mPa | -- | -- |
| Charpy impact strength at 1eU unnotched
|
20 | KJ/m2 | ISO 179 | -- |
| Charpy impact strength at 1eA notched
|
1.4 | KJ/m2 | -- | -- |
| Vicat softening temperature at B50 | 107 | °C | ISO 306 | -- |
| Heat distortion temperature at 1.8 MPa | 102 | °C | ISO 75 | -- |
| Thermal expansion coefficient | 6 x 10^-5 | 1/°C | ISO 11359 | -- |
| Transmittance at 3 mm | 92 | % | ISO 13468 | -- |
| Haze at 3 mm | < 0.5 | % | ISO 14782 | -- |
| Refractive Index | 1.49 | -- | ISO 489 | -- |
| Flame Rating 1.5 mm/3.0 mm | HB | Class | UL94 | -- |
| Surface resistivity | >10^16 | Ω | ASTM D 527 | -- |
| Volume Resistivity | >10^13 | Ω.m | -- | -- |
| Dielectric strength at 4 kv/sec | -- | kV/mm | ASTM D 149 | -- |
| Dielectric constant at 60 Hz | 3.7 | -- | ASTM D 150 | -- |
| Drying Temperature | 80 - 90 | °C | -- | -- |
| Drying Time | 3 - 4 | h | -- | -- |
| Injection Temperature | 220 - 260 | °C | -- | -- |
| Mold temperature | 50 - 90 | °C | -- | -- |
| Melt flow rate at 230 °C/3.8 Kg | 14 | g/10min | ISO 1133 | -- |
| Shrinkage | 0.2 - 0.6 | % | ISO 294 | -- |
| Water absorption at 24hr | 0.3 | % | ISO 62 | -- |
| Density | 1.19 | g/cm3 | ISO 1183 | -- |
| Tensile strength at 5 mm/min | 67 | mPa | ISO 527 | -- |
| Tensile Modulus at 1 mm/min | 3300 | mPa | -- | -- |
| Elongation at 5 mm/min | 4 | % | -- | -- |
| Flexural Strength at 2 mm/min | 120 | mPa | ISO 178 | -- |
| Flexural Modulus at 2 mm/min | -- | mPa | -- | -- |
| Charpy impact strength at 1eU unnotched | 20 | KJ/m2 | ISO 179 | -- |
| Charpy impact strength at 1eA notched | 1.4 | KJ/m2 | -- | -- |
| Vicat softening temperature at B50 | 89 | °C | ISO 306 | -- |
| Heat distortion temperature at 1.8MPa | 84 | °C | ISO 75 | -- |
| Thermal expansion coefficient | 6 x 10^-5 | 1/°C | ISO 11359 | -- |
| Transmittance at 3mm | 92 | % | ISO 13468 | -- |
| Haze at 3 mm | < 0.5 | % | ISO 14782 | -- |
| Refractive Index | 1.49 | -- | ISO 489 | -- |
| Flame Rating 1.5 mm/3.0 mm | HB | Class | UL94 | -- |
| Surface resistivity | >10^16 | Ω | ASTM D 527 | -- |
| Volume Resistivity | >10^13 | Ω.m | -- | -- |
| Dielectric strength at 4 kv/sec | -- | kV/mm | ASTM D 149 | -- |
| Dielectric constant at 60 Hz | 3.7 | -- | ASTM D 150 | -- |
| Drying Temperature | 70 - 80 | °C | -- | -- |
| Drying Time | 4 - 6 | h | -- | -- |
| Injection Temperature | 220 - 260 | °C | -- | -- |
| Mold temperature | 60 - 90 | °C | -- | -- |
| Melt flow rate at 230 °C/3.8 Kg | 1.5 | g/10min | ISO 1133 | -- |
| Shrinkage | 0.2 - 0.6 | % | ISO 294 | -- |
| Water absorption at 24hr | 0.3 | % | ISO 62 | -- |
| Density | 1.19 | g/cm3 | ISO 1183 | -- |
| Tensile strength at 5 mm/min | 75 | mPa | ISO 527 | -- |
| Tensile Modulus at 1 mm/min | 3300 | mPa | -- | -- |
| Elongation at 5 mm/min | 6 | % | -- | -- |
| Flexural Strength at 2 mm/min | 130 | mPa | ISO 178 | -- |
| Flexural Modulus at 2 mm/min | 3400 | mPa | -- | -- |
| Charpy impact strength at 1eU unnotched | 20 | KJ/m2 | ISO 179 | -- |
| Charpy impact strength at 1eA notched | 1.6 | KJ/m2 | -- | -- |
| Vicat softening temperature at B50 | 101 | °C | ISO 306 | -- |
| Heat distortion temperature at 1.8MPa | 94 | °C | ISO 75 | -- |
| Thermal expansion coefficient | 6 x 10^-5 | 1/°C | ISO 11359 | -- |
| Transmittance at 3mm | 92 | % | ISO 13468 | -- |
| Haze at 3 mm | < 0.5 | % | ISO 14782 | -- |
| Refractive Index | 1.49 | -- | ISO 489 | -- |
| Flame Rating 1.5 mm/3.0 mm | HB | Class | UL94 | -- |
| Surface resistivity | >10^16 | Ω | ASTM D 527 | -- |
| Volume Resistivity | >10^13 | Ω.m | -- | -- |
| Dielectric strength at 4 kv/sec | -- | kV/mm | ASTM D 149 | -- |
| Dielectric constant at 60 Hz | 3.7 | -- | ASTM D 150 | -- |
| Screw L/D | 25 ~ 35 | -- | -- | -- |
| Barrel temperature (Hopper) | 210 - 240 | °C | -- | -- |
| Barrel temperature (Center) | 220 - 250 | °C | -- | -- |
| Barrel temperature (Die side) | -- | °C | -- | -- |
| Die temperature | -- | °C | -- | -- |
Q1. Are you a factory or trading company?
Q2. Can I get samples for testing?
A: Yes, we provide samples. Customers cover the initial shipping costs, which are reimbursed in our first cooperation.
Q3. How does your factory ensure quality control?
A: Our factory is ISO9001:2008, REACH, and FAMIQS certified, ensuring rigorous quality control. Each Batch of goods do SGS inspection before leaving our factory.
Q4. What's your Delivery Time?
A: Delivery typically takes 5 to 10 days after payment receipt. Larger orders are confirmed with our production department for prompt, quality-assured delivery.
Q5. What are your payment terms?
A: We accept L/C, T/T, Western Union, and Paypal. Alternative methods can be discussed.
Q6. Which documents do you provide?
A: Standard documents include Commercial Invoice, Price List, Packing List, COA, Origin Certificate, Quality/Quantity Certificate, Beneficiary's Certificate, MSDS, B/L, and others upon request.
Additional Information:
){kind=link}